Fabrication of three dimensional open porous regular structure of PA-2200 for enhanced strength of scaffold using selective laser sintering

Scaffolds are essentially required to have open porous structure for facilitating bone to grow. They are generally placed on those bone defective/fractured sites which are more prone to compressive loading. Open porous structure lacks in strength in comparison to solid. Selective laser sintering (SLS) process is prominently used for fabrication of polymer/composite scaffolds. So, this paper aims to study for fabrication of three-dimensional open porous scaffolds with enhanced strength, process parameters of SLS of a biocompatible material are required to be optimized.

Regular open porous structures with suitable pore size as per computer-aided design models were fabricated using SLS. Polyamide (PA-2200) was used to fabricate the specimen/scaffold. To optimize the strength of the designed structure, response surface methodology was used to design the experiments. Specimens as per ASTM D695 were fabricated using SLS and compressive testing was carried out. Analysis of variance was done for estimating contribution of individual process parameters. Optimized process parameters were obtained using a trust region algorithm and correlated with experimental results. Accuracy of the fabricated specimen/scaffold was also assessed in terms of IT grades. In vitro cell culture on the fabricated structures confirmed the biocompatibility of polyamide (PA-2200).

Optimized process parameters for open cell process structures were obtained and confirmed experimentally. Laser power, hatch spacing and layer thickness have contributed more in the porous part’s strength than scan speed. The accuracy of the order of IT16 has been found for all functional dimensions. Cell growth and proliferation confirmed biocompatibility of polyamide (PA-2200) for scaffold applications.

This paper demonstrates the biocompatibility of PA-2200 for scaffold applications. The optimized process parameters of SLS process for open cell structure having pore size 1.2 × 1.2 mm² with strut diameter of 1 mm have been obtained. The accuracy of the order of IT16 was obtained at the optimized process factors.