Preparation and performances of coated and aluminous entry boards with water-soluble resins for PCB drilling

Abstract

Purpose

This paper aims to provide a new drilling entry board for printed circuit board (PCB) process, superior in heat dissipation, lubrication, water solubility and hole location accuracy, achieving an excellent drilling process.

Design/methodology/approach

Using a mixture of polyethylene glycol (PEG) and water-soluble adhesives as hydrosoluble, endothermic and lubricant resins and aluminum foils as baseplates, a series of coated and aluminous entry boards (CABs) for PCB drilling was successfully prepared. The surface appearance of the entry boards was observed clearly by scanning electron microscopy (SEM). The endothermic and lubricant effects of the resins applied on the CABs was characterized by differential scanning calorimetry (DSC) and their water solubility was tested in the normal-temperature water (25°C). Moreover, the CABs’ good drilling properties were tested when they were used for PCB drilling.

Findings

The SEM analysis showed that the surfaces of the resin layers coated on the CABs whose coating thicknesses were less than 80 μm were smoother and flatter, which could improve hole location accuracy and reduce drill breakage ratio. By virtue of DSC, the endothermic and lubricant effects of the CABs were proven. The fusion of PEG in the resin layers could absorb the heat produced by drilling, restrain the temperature of the drill bit and hole rising and lubricate the drill bit efficiently when a hole was being drilled, which could achieve high-quality holes with good production efficiency. The water-soluble test showed that the prepared CABs had excellent water solubility at normal temperature, enabling the resin left on the hole walls and in the flute of the drill bit to be washed away easily and thereby improving the drilling efficiency and quality. The drilling tests showed that the increase in the thickness of the CABs’ coating could improve the hole location accuracy and alleviate the bit wear. In addition, the suitable coating thickness could ensure the firm adhering of the resin coating the aluminum foil, effectively avoid drill intertwist and prevent the resin debris from blocking the drilled holes on the surface of the entry board, which could hinder chip removal, resulting in poor hole wall quality and drill breakage.

Originality/value

This paper has a remarkably high industrial practicality in the PCB manufacture process.

Citation