Effect of element contents on friction and wear behaviors of ternary nitride coatings

Abstract

Purpose

The purpose of this study was to clarify the applicable conditions for coatings with different element contents. Surface coating on existed tool material is an effective way to improve the cutting tool properties in extremely adverse machining conditions. These coatings are generally non-metering compounds. Each coating with a certain element ratio has a specific application condition, and the relationship between element contents and performance should be defined.

Design/methodology/approach

(Zr, Ti)N hard coatings with different element contents were deposited on cemented carbide. The ball-on-disk method reciprocating sliding wear tests against 40Cr hardened steel were carried out. This paper was focused on analysis of the friction and wear behaviors of these (Zr, Ti)N coatings with different element contents.

Findings

The results indicated that atomic ratio of Zr and Ti was the main factor that decided the friction coefficients. The friction coefficient and wear rate showed a gradual downward trend at 10 N with the increase of Zr content. The wear rate was the smallest at the atomic percentage of nitrogen 0.466. If the lattice distortion of the coatings gets too severe, the coatings would have a high wear rate.

Originality/value

The optimal application conditions of the coatings were defined, and this was important for customized design or choice of the coatings under different cutting parameters.

Citation

Yan, P., Wang, X. and Jiao, L. (2016), "Effect of element contents on friction and wear behaviors of ternary nitride coatings", Industrial Lubrication and Tribology, Vol. 68 No. 6, pp. 696-701. https://doi.org/10.1108/ILT-07-2015-0099