An experimental study for using nano-alumina to improving mechanical properties of epoxy resin for assembling glass artifacts

Abstract

Purpose

This study aims to assess the efficacy of nano-alumina (nano-Al₂O₃) in improving the performance of epoxy adhesives used to assemble archaeological glass. The conservators face a significant problem in assembling this type of artifact. Therefore, the assembling process is considered one of the important stages that must be taken care of to preserve these artifacts from damage and loss.

Design/methodology/approach

To evaluate the stability of adhesives, the samples were subjected to artificial aging under varying environmental conditions. Some investigative techniques and mechanical testing were used in this study to evaluate the selected materials. It includes a transmission electron microscope, X-ray diffraction, visual assessment, digital microscope, scanning electron microscopy (SEM), color change and tensile strength test.

Findings

The visual evaluation and the digital microscope results showed that the epoxy/nano-Al₂O₃ greatly resisted artificial aging. Although slight yellowing was present, it did not significantly affect the general appearance of the samples. On the other hand, the pure epoxy sample showed cracks of different sizes on its surface due to aging, as evidenced by SEM examination. Furthermore, epoxy/nano-Al₂O₃ has a better tensile strength (11.27 MPa) and slight color change (ΔE = 2.06).

Originality/value

The main objective of the experimental study was to identify appropriate adhesive materials that possess key properties such as non-yellowing and improved tensile strength by conducting various tests and evaluations. Ultimately, the goal was to identify materials that could serve as effective adhesives for assembling the archaeological glass.

Citation

Eloriby, R.A.G. and Mohamed, H.M. (2023), "An experimental study for using nano-alumina to improving mechanical properties of epoxy resin for assembling glass artifacts", Pigment & Resin Technology, Vol. ahead-of-print No. ahead-of-print. https://doi.org/10.1108/PRT-07-2023-0064